引用本文格式: Li Zhi-Hong,Tang Jia-Wei,Guo Xiang,Wang Yi,Luo Zi-Jiang,Ma Ming-Ming,Huang Yan-Bin,Zhang Zhen-Dong,Ding Zhao. The Effect of Ga Droplet Deposition Amount on Morphology of Concentric Quantum Double Rings [J]. J. At. Mol. Phys., 2020, 37: 261 (in Chinese) [李志宏,汤佳伟,郭祥,王一,罗子江,马明明,黄延彬,张振东,丁召. Ga液滴沉积量对GaAs/GaAs(001)同心量子双环形貌的影响 [J]. 原子与分子物理学报, 2020, 37: 261]
 
Ga液滴沉积量对GaAs/GaAs(001)同心量子双环形貌的影响
The Effect of Ga Droplet Deposition Amount on Morphology of Concentric Quantum Double Rings
摘要点击 47  全文点击 5  投稿时间:2019-01-18  修订日期:2019-02-25
查看全文  查看/发表评论  下载PDF阅读器
DOI编号   
中文关键词   Ga液滴沉积量  同心量子双环  液滴外延
英文关键词   Ga Droplet Deposition  CQDRs  Droplet Epitaxy
基金项目   国家自然科学基金
作者单位E-mail
李志宏 贵州大学大数据与信息工程学院 1914106037@qq.com 
汤佳伟 贵州大学大数据与信息工程学院 2108393194@qq.com 
郭祥 贵州大学大数据与信息工程学院 516412261@qq.com 
王一 贵州大学大数据与信息工程学院 381429761@qq.com 
罗子江 贵州财经大学信息学院 172787007@qq.com 
马明明 贵州大学大数据与信息工程学院 914945535@qq.com 
黄延彬 贵州大学大数据与信息工程学院 875904240@qq.com 
张振东 贵州大学大数据与信息工程学院 455563822@qq.com 
丁召 贵州大学大数据与信息工程学院 zding@gzu.edu.cn 
中文摘要
    通过液滴外延法制备了GaAs/GaAs(001)同心量子双环(Concentric Quantum Double Rings, CQDRs),研究了Ga液滴沉积量对CQDRs的影响。研究结果发现:随着Ga液滴沉积量的增加,CQDRs密度降低,内环高度增高,外环高度降低,中心孔洞深度增加。CQDRs内环拟合结果表明,Ga液滴沉积量少于0.92ML(Monolayer, ML)时无法成环;外环拟合结果显示,在本实验条件下,形成外环的最小Ga液滴沉积量为3.1ML。拟合结果与实验结果一致,相关研究结果对液滴外延法制备GaAs同心量子双环具有指导意义。
英文摘要
    In this paper, GaAs/GaAs(001) Concentric Quantum Double Rings (CQDRs) were prepared by droplet epitaxy, and the effect of Ga droplet deposition amount on CQDRs was studied. The results show that with the increase of Ga droplet deposition, the density of CQDRs decreases, meanwhile the height of inner ring increases, along with the height of the outer ring decreases, and the depth of the center hole increases. The fitting results for inner ring of CQDRs suggest that Ga droplet cannot form a ring if the deposition amount is less than 0.92ML. The outer ring fitting results reveal that the minimum Ga droplet deposition amount to form the outer ring is 3.1ML under the experimental conditions. The fitting results are consistent with the experimental results,and the related research results have guiding significance for the fabrication of GaAs concentric quantum double rings by droplet epitaxy.